Stainless Steel Coil Metal Slitting and Toll Processing

stainless steel 301 - coil slitting

Stainless Steel Coil Stock Supplier

With its chromium-nickel base, Type 301 is an austenitic alloy applicable for a variety of uses. High corrosion and abrasion resistance, forming and drawing qualities, weldability, strength and ductility make Type 301 a highly marketable product. It is hardened only by cold working, not by heat-treatment, as are all high chromium-nickel steels. It is nonmagnetic in the annealed state yet Type 301 becomes slightly magnetic with progressive cold working. Applications include aircraft parts, architectural trim, automobile trim and wheel covers, construction components, high temperature, light gauge structural members, roof drainage, thermostatic and transportation equipment.

chemical composition limits (%)

Carbon C	Manganese Mn	Phosphorus P	Sulfur S	Silicon Si	Chromium Cr	Nickel Ni	Nitrogen N
0.15	2.00	0.045	0.030	1.00	16.00-18.00	6.00-8.00	-

Representative mechanical property

	KSi	MPa	ksi	mpa	in 2 inches %
Annealed ¼ Hard ½ Hard ¾ Hard Full Hard Extra Full Hard	75 125 150 175 185 200	(758) (862) (1034) (1207) (1276) (1379)	40 75 110 135 140 160	(276) (517) (758) (931) (965) (1103)	58 25 18 12 9 2	B 70-90. C-25 C-30 C-35 C-41 C-46 Nom.
*Minimum Chemical composition is percent maximum unless shown as a range or a minimum. Information presented as a guide for reference purposes only and is not intended for product design or application.